Re: crystallization instainless steel

LaGrecaColonna wrote:
> 
> I have to mesure the recrystallized volume fraction.

Metallography or texture analysis. If yout material was 100% austenie
prior to cold deformation and has transformed to martensite completly,
it will retransform to austenite during recrystallization. You can then
assume : %austenite = %recrystallized

Michael Dahms